gENERAL DESCRIPTION
Kobatek 352 has a manganese alloyed stainless steel deposit containing Cr/Ni/Mn/Mo which is a work hardening alloy. It is used for build-up applications and cushion layers prior to harder overlays, and for a wide range of steel, low alloy steel and 12-14 % austenitic manganese steel components subjected to severe impact combined with high pressure. Steel deposit will also resist a wide range of corrosive conditions and cavitation.
Deposits exhibit a smooth even shaped bead, high metal recovery rates and ease of slag removal. The electrode can be deposited in contact with the workpiece.
Mechanical Properties, Typical, All Weld Metal
Tensile Strength | : | 64 – 66 | (N/mm²) | ||
---|---|---|---|---|---|
Elongation (L=5d) | : | 40 – 44 | (%) | ||
Hardness | : | 160 – 200 | (HB) | (as welded) | |
400 – 440 | (HB) | (work hardened) |
Approvals and Certificates
Certificates
GOST | TSEK |
Application Areas
- Welding and repairing 12-14 % manganese steels
- Crusher jaws
- Tractor sprocket tooth
- Guides and rollers on tracked vehicles
- Armour plates
- Perforated plating on ore-sorters
- Gyratory crusher cones
- Conveyor rollers
- Crusher cylinder hooks
- Dozer cutting edges
- Bucket lips and sides
- Impactors, hammers
- Joining austenitic manganese steels to carbon steels
- Stainless cladding carbon steels and low alloy steels
Welding Parameters / Packing and Diameter Informations
Current Type and Polarity : DC (+) / AC
Diameter x Length (mm) |
Procedure – A Current (Amper) |
Procedure – B Current (Amper) |
Weight (kg/box) |
---|---|---|---|
3.25 x 350 |
140 – 160 | 100 – 160 | 5 |
4.00 x 350 |
210 – 240 | 140 – 190 | 5 |
PROCEDURE – A
High Amperage Welding
High amperage welding for heavy sections and large parts, maximum deposition rates.
PROCEDURE – B
Low Amperage Welding
Low amperage welding for small sections and parts which must not be overheated, minimum dilution and low heat input.